A good crimp junction is better than a bad solder joint. I like to solder sometimes, but on somethings, I would rather crimp. I know that experienced technicians know how to make a good solder joint. They know what size solder to use (including core type and percentage) what size iron or gun to use and how hot it needs to be. If you get all those right & tin the wires before connecting them, there will be no need to twist them, and being pre-tinned will mean you don't have to add as much solder when making the joint, which means less time with the iron on the wire. More surface contact between the tip and wire decreases time also. Beyond that, aluminum makes the best heat sink. It conducts heat very well, but doesn't hold the heat very long. But, everything between the iron and the heat sink will get hot, so moving them to the end of the insulation will also deter the solder from creeping up the wire. HOWEVER, it's very likely that most DIYers are not going to have the soldering skills of an experienced A/P mechanic, or electronic technician. Crimping can be mastered much easier and quicker than soldering, which makes it the best option for most people.

As an ex Air Force missile technician I was trained to solder to NASA HRHS (High Reliability Hand Soldering) technique. You can crimp all you want I will continue to solder without failure.

I am 74 years old. I built my first crystal radio at age 8. I have spent my entire life in consumer and industrial electronics. I solder EVERYTHING. I usually even solder crimp terminals. If you are having problems soldering items together, use the best solder, always use solder flux, always prepare the work target-wire-terminals-get them clean and shiny. Use a good clean soldering iron ( or gun, love my 25 year old weller gun for big stuff ). Don't rush an iron, let it get to temperature. Always remember you are soldering the wire, not the solder. The objective is to get the work piece hot enough to flow the solder onto it. Learn how to solder.

As a 40 year electric forklifts mechanic I soldered connections for used in all kinds of corrosive environments. I never had a failure as opposed to some of my counterparts who relied on crimp joints that saw failures. Properly soldered and installed wire connections will not fail. Crimped connections also fail due to heat from bad connection.

Nearly sixty years ago, my Dad taught me how to solder. He'd been a radar technician on a carrier in WWII and learned the importance of making a strong mechanical connection before actually soldering. Admittedly, warship techniques may be overkill for ordinary work, but I've never had a proper solder joint fail, which is more than I can say for crimp connections.

Man, I've been doing it wrong for 50 years. Thank you for your insight and showing me the error of my ways. In a prior life I used to do mobile electronics installations (audio, 2-way radio's) and I soldered all wiring under 16ga. The technique I always used was to clean/flux/tin the wires, apply heat shrink tubing to each individual joint, and if possible, another larger piece of tubing over the entire cable, lay the wires parallel (never twist - makes the joint too large), solder them together with LEADED solder - no-lead solder is a lot more brittle. Rinse/repeat for all the other wires, apply dielectric grease over the joints, slide the HS over the joint & shrink with hot air - NEVER use an open flame. The excess grease should squeeze out the ends. Once all the individual wires have been soldered/greased/shrunk then apply an additional layer of dielectric grease over/around all the splices, then slide the outer tubing over the repaired area and shrink that down. If it's in a harness, I still pack the joints with grease then use high quality electrical tape over the entire harness to help protect the joints. For wiring that's more exposed, I'll use 3M mastic tape instead of electrical tape for addition protection. I've found that it works better if I heat it up with my heat gun before applying it. Once the repairs are complete, I use plenty of wire ties to mechanically secure the harness from flapping in the breeze to prevent stresses on the wiring to concentrate at the joints. If it's just a few wires I'll take a bit of larger, solid wire and tape it parallel with the wire(s) extending past the joint on both sides to provide mechanical support and prevent any flexing @ the joints. I've done thousands of joints on cars, trucks, boats, trailers, motorcycles, mowers, CNC forklifts, machining centers etc. using these techniques and as far as I know, not a single joint has ever failed. To be clear, I use crimp connectors & ferrules all the time, but usually when it's in a dry environment, and typically to terminate wiring, rarely for splicing. The bottom line is it doesn't matter if you crimp or solder the connections as long as you do it correctly. Just because a lot of folks do it wrong doesn't mean you should "NEVER" do it as you imply. In fact, in the 50 years I've been working on things, I've had several orders of magnitude more issues with people's crimp connections than I have soldered ones. If you do nothing to protect the joint from the elements, a crimped connection will fail quicker than a soldered one due to moisture ingress and corrosion. This is especially true up here in the north where tons of salt is dumped on the roads in the winter. I've seen exposed crimped connections fail in less than a year due to salt corrosion. Crimped connections do tolerate mechanical stresses better, but again it's down to proper technique and providing mechanical support. But the most often missed step on exposed connections is dielectric grease. I don't think I've ever seen anybody doing 'repair' videos use it. I see some folks like this video advocating adhesive lined shrink tubing and it's certainly better than nothing but not something I'd recommend. Besides being a lot less common and more expensive than plain HS tubing, it's only going to be effective if your wiring is clean, and only if it's a single, individual wire that the tubing can shrink completely down to without any gaps. Too often I'm doing multiple wires or different sized wires where I won't get a complete seal with the tubing. If you use dielectric grease then it doesn't matter if there's any gaps, the grease completely fills the voids when it gets shrunk down. The butt splice connectors that come with DE grease and shrink tubing that you showed are pricey, but the best alternative for folks that don't do this sort of work often.

In the aviation electronics industry, we were taught (as inspectors) to be aware of solder migrating under the insulation, for the exact reasons you stated- after some vibration, the wire will break. Good video! Thanks.

While your soldering joint is OK, a couple of tips... 1. Use flux. Liberally apply flux to the wires before soldering. The rosin core of your solder isn't enough. 2. Twist the wires into a Lineman's Splice before soldering. The Lineman's Splice is stronger than the wires themselves. This step insures that there is no way the splice will fail before the wire will. Adding the solder to the Lineman's Splice will aid in lowering electrical resistance. Adding this step to your soldered wire joints is a complete game changer, and it is not difficult to do. Using flux, a Lineman's Splice, and solder will result in a joint with less electrical resistance than any crimped solution out there, and far stronger than crimping. And it might very well be over kill. There's nothing wrong with a properly crimped joint, either. This is a situation in which there is no real "correct" answer. Properly soldered or properly crimped is just fine for automotive electrical work, as long as either joint type is done correctly. Source: I'm 56 years old, and have been soldering and/or crimping wiring harnesses on a wide variety of things... cars, trucks, tractors, trailers, RV's since I was 16. I have also done a lot of car audio installations. While I do stand by my above statement about there being no one "correct" solution, there is an exception to that rule: I *always* have and *always* will solder connections for car audio or alarm system installations to achieve the lowest electrical resistance possible across a joint.

The fellow who does a hack job with soldering is also likely to do the same with the crimp. Attention to detail is key with anything and if you don't have that, the end result will be the same.

Don't forget to put the heatshrink tubing on BEFORE you crimp! Ask me how I know!

If you wick solder past the wire insulation, it is due to very poor tools and/or technique. This usually is caused by using too small a wattage iron which means you have to heat the wire far too long letting the heat extend well down the wire. It can also be caused by simply adding in far too much solder. A high wattage iron will heat the join area very quickly and the soldering will be done before the heat and solder can wick down the wire under the insulation. And you need very little solder. And if you apply shrink tube to provide some additional strain relief past the insulation, issues with vibration and fatigue breakage simply aren’t an issue. These issues are due to poor technique. A quick summary: 1. Poor soldering is a bad way to splice wires. 2. Poor crimping is a bad way to splice wires. 3. Good soldering is a good way to splice wires. 4. Good crimping is a good way to splice wires. I personally like both methods, but use crimping more simply due to its convenience and speed. You can work in the field without need for electrical power of any sort and crimping is pretty fast with the right tools and a little practice. However, if I need a super reliable, super strong and low resistance connection, I will use solder every time. One thing I have wanted to do, but have yet to invest time in is testing soldered splices vs. crimped splices for both resistance and pull strength. I strongly suspect that solder would win both contests and I saw one UKpostsr who did the resistance test and solder clearly won that, but, as I recall, he did not strength test the connections which would have completed the puzzle.

Thank you for posting how the unisolated crimps work and with the special type of pliers. I definitely learned something and will be picking up a crimper set for them.

For joining wire ends, crimping makes a ton of sense. For integration I prefer solder since it would require you to cut the factory wire. Different techniques for different applications. Great video!

Been a aircraft tech for 30 years, and that crimp connection will break easier at the crimp than the solder one will. We do crimp on aircraft, but they are environmental crimps with crimpers that are calibrated. I still prefer a good hot solder to any crimp. We used to use those crimps you like on our strobe lights, but got away from them. Failure rate was high. I will never be convinced a crimp is better than a solder. Twist that crimp joint like you did with the solder joint.

Thanks for the advice homie! I’ve connected 100’s of wires working on classic cars over 20 years and if you use good thick shrink tubing, that wire is not gonna bend at the solder point causing a break like you illustrate in my experience. Having said that, sometime I just don’t have the space to solder. If I use a crimp connector, also use good shrink tubing but if it’s on the outside of the car I’ll also add liquid electrical “tape” on top of that. Never had a problem

Having over 40 years experience working in electronics and being a backyard mechanic I think the most important message you could give would be that you should do what not only works best for you but has the best chance of long term success. There are places I wouldn't trust solder, and for simplicity a lot of my work uses a good quality heat shrink crimp. But anything I can bench I still prefer to use solder.

I wish you would have tested the resistance of the various connectors and the solder.....that is a very important aspect, especially if you're dealing with something like a signal wire.

When I worked for GM, they would include the crimp/seal splices in connector repair kits. They included in their electrical repair kits that were shipped to the dealer with a set of ratcheting crimpers. They work perfect and never failed me once. That's why I bought a pair online from crimp supply. They are a little pricey, but worth the money because of how well they work.

Thanks for the video Irvin, we don't splice wires using soldering either on aircraft, we use Tyco Raychem D-200 MiniSeal Crimp Splices, which are similar to what you demonstrated.

Everything about this video was amazing! Straight to the point and informative, showed what you meant as well as explained what you meant, and packed it with good info. Thanks for this!

GREAT VIDEO! Tip for basic crimp connector shown at 9:00 & 10:40 : There is provision for an insulation crimp; beyond the metal barrel about midway on the belled ends. Some of the flat metal style crimpers have another 'die' at the tip marked 'ins'. This will add some support to the wire. I agree with much of what you say. I am a professional, and I prefer soldering, but I totally agree that a DIY MUST have sufficient skills and 'finesse' if they are going to solder connections. The huge issue is having CLEAN copper wires. Many repairs are on old or existing wire, which are aged, and have a tarnish fro air and insulation outgassing. This MUST be cleaned until the wires shine like a new penny for the solder to actually bond properly. (should look like brand new striped wire gleam). Small wire brush (toothbrush) or sand paper. And if it is stranded, then you have to 'squash' the strands flat from multiple directions, cleaning it each time, to get to the interior strand surfaces (very difficult BTDT). Otherwise the solder is only going to grab the outside surface strands (and only on their outside faces), and only the outside strands will be conduction the current! Two technical tips: Iron tip life can be shortened by overly frequent tinning. Solder slowly dissolves the iron cladding (or very fast on copper, in the case of solid copper tips). If it looks as good as the tip you showed, and takes solder readily while soldering, then I would use it as is. When it has scale or solder beads up and does not flow onto the tip while soldering, clean or re-tin it then. [sometimes if the tip gets neglected or won't tin, I wire-wheel it, followed with proper tinning...] With experience and skill, you can limit how far the solder 'wicks' up inside the insulation. This is difficult to do in one motion without getting a 'cold' joint in the center (bad, 'unstuck' solder). This is done adding minimal solder to the center and staying there a second or two until it penetrates there and bonds. Then add more solder running the tip out to the ends, tinning the entire joint, and stopping when you see it reach the insulation. Remove the tip then before it runs up under the insulation too far. Your technique is very good.

I've started to crimp more wires now than solder the last handful of years exactly because of the problem you showed with the wire breaking. Solder is brittle and can create a sharp bend radius point and break the wire as well. If you have good strain relief and wire securement, this can be nearly eliminated. I've also learned somewhat recently how much of a difference a good iron makes. A digital soldering iron like you have that regulates temp can make a way better joint. One thing I do to make sure my crimps don't develop any corrosion and/or resistance is to dip the wire end in dielectric grease. That fills in the microscopic voids in the metal to keep out air and moisture. The pressure of the crimp moves the grease out of the way from metal-to-metal contact. I can't measure any resistance difference. Then I'll follow up (after a pull test) with some adhesive lined heat shrink.

Nice video. I would like to add that the ratcheting feature of the better crimper will help ensure repeatably good crimps. When doing a bunch of crimping one's hand can get tired. So without the ratchet feature the first crimp is likely to be a better crimp than the last. The ratcheting crimpers don't let go if you don't crimp hard enough. Go for a quality ratcheting crimper all the time, and it is good that the ratcheting crimp tools aren't $300+ each anymore.

Essentially ran across this by accident, but I'm glad I did. I have run into the problems that you've described, this is really good information. I have some electrical work to do in my car and have been worried by the integrity of the connection exactly as you've described. This is very good information.

Thanks for sharing. Crimp is not only the way to go for a solid connection but also looks good and is a total pleasure to do if you just spend 5min to learn to do it right.

There is one reason and only one reason why OE manufacturers crimp instead of solder - it costs less to crimp. If soldering was less expensive, the OE manufacturers would solder. It has nothing to do with crimping being "superior" to soldering. Circuit boards are soldered because it is the least expensive way to produce them. I solder small gauge wires (after crimping them if using a connector) and I hydraulic crimp large gauge wires for my car. It is harder and more time consuming to make a good looking wire to wire solder joint (mostly in the twisting of the wires), but somehow more satisfying.

OEMs use crimps because it's quicker than trying to heat up every single connection and solder it. For speaker wires crimps are fine but for larger gauge cables and heavier currents, you should definitely solder stuff. It's not about how strong the connection is, but how much current can flow through, and what your resistance looks like.

very good video, totally agree with ya on soldering. few people do it right, also takes longer. but as a retired service tech for MOPAR products, i always crimped and soldered splices with sealing heat shrink. which was per MOPAR wire repair standard.

Crimping, when done correctly, and with a good quality terminal, is the BEST way to connect wires to each other, and to terminals. Period. Gas tight joints result, which is what you want, and is what all the car manufacturers use. Good video.

6:55 The solder spike on the joint is something to watch out for also; that can happen with insufficiently heated joints as the iron pulls away and leaves with the solder trailing behind. Or if the wire wrapping isn't done carefully, with individual strands of wire poking outwards. That can end up piercing the heat shrink and could potentially short out to something.

Thank you so much for this video. I was dreading the thought of soldering hundreds of 22 ga wires cut from an auto harness. Using the open barrel crimp method will reduce the time needed by 10x! Works great.

Thanks for this video. What kind of crimp do you recommend for a removable connection, like a wire connecting to a relay? Cheers.

Crimping does has its advantages when working on auto electricals, when techs/mechs are inside tight spaces like under the dashboard. An iron in that space is challenging, if not problematic. Extra care is a must, to avoid burning the carpet or melting the plastics. Also, the repaired joint, soldered or crimped, must be away from any locations where it will be bent, pulled or strained. Thanks for sharing!

The reason behind tinning is so you don't end up getting an oxidation layer on your iron. Also you should be doing it AFTER every time you use the iron

Dont really work with wires much, but i am changing out some lights in the future so nice to know!☺️

Great video, got another race loom to do and was finding more tips and tricks. Been soldering my race looms for years and with the heavy vibrations and crashes they break at the ends of the solder all the time . However my crimps always have the flex to keep the connection. A national super bike team told me never to solder a race bike as there's too much stress's and vibrations on the loom at 300km/hr . Paid an auto electrician to put in a trailer wire loom they soldered and guess what it failed within 5 years on the solder joints. . ten years later my crimps still hold.

You are a great instructor. Clear explanations with demos. Hope to see more videos like this. Thank you.

Well... I've been doing electrical work on cars for a long time....and for the first years I did a lot of twisting and electrical tape... I'm not proud of it.. but it work.. in a perfect world I would use your method, but a lot of times the place the repair needs to be made is tight. Either soldering or crimping make the joint rigid and can break.. for thick cables I crimp with a hydraulic crimper... everything else I solder... and about a year ago I started using the heat shrink that has built in solder ring and weather proof ends. In my opinion, way better than conventional soldering and wayyyyy better than crimping. More flexible, easier to do, look a lot more professional....

I've been a professional mechanic for over forty years, so commenting on idiots making "how to" youtube videos is not unknown for me to do. LOL. So when I saw this one I decided, let's see how I can rip this guy a new one. Great job Irvin!!!! Well done. However, every splice no matter how it's done will end with a hard point that with vibration or flexing will break at that point. Heat shrink that extends beyond the hard point will serve as a flexible strain relief whether it is soldered or crimped. You are correct about solder creep, you just have to be conservative with the solder which can be really tough to do when you turn the splice over and see a bare spot. If it is a highly flexed area I would replace the whole section of harness so that the splice can be in an area that can be zip tied down P.S. the thickness of the Snap On crimp/strippers is also the length of bare wire you should have after stripping. So when you put the wire in the stripping area, don't let it protrude any more than the thickness of the handle.

Great and informative video. I'm curious what process you use to tap into an existing wire to form a T-connection? I have a project where I need to do this in a very confined space.

I perfer crimping over soldering. i purchased a pioneer avh3500nex with pioneer backup camera. I ordered everything the same you got. Carpi strippers, and keeyees connectors came in today, waiting on the crimping ratcheting tool. Already have heat shrink. Imma give it a go. Great video 👌👌👍👍

Can you do the bent test on your crimp wire. Same test as you did for the soldering wire.

I agree with everything in this video. Non-insolated connectors are the only style we use at work too for the very same reasons you highlighted. I've never seen oem employ any other method

Agreed. I also like heat shrink butt connectors as my general use splice connection. I'd definitely recommend getting ratcheting crimpers for insulated connectors though. It really doesn't take much to step up to the next level of wiring with open barrel crimps like you showed. People need to watch a few tutorial videos and buy a couple tools. When people with knowledge say crimping is better, they aren't talking about hardware store crimps with hard plastic open ended insulation and a $5 thin metal crimping tool. The issues with both connection methods generally boil down to user error and incorrect equipment. Trying to solder with bad technique or the wrong tip will usually result in a bad joint. Trying to crimp without the enough knowledge or the correct crimping tool can also result in a bad connection. As a general rule, crimping is harder to mess up and easier to check for correct application. There is less overall room for error. That said, most people don't even do the bare minimum of research and tool investment for crimping. Wiring really takes some learning above all else. I did add a dab of solder to some spade terminals recently after crimping 10 gauge wire into them. I only did it because I didn't have the exact right crimping tool and did not want the wire to be able to wiggle. The key is I still made sure to heat the wire and terminal to melt the solder rather than using the iron. I also only applied just enough solder to surround the wire in the crimp and did not allow any to wick past the strain relief. Very rarely will I solder anything automotive.

I loved your wire nut rant 😂 straight up pulled a sub for the comedic side of this video, but this was the most in depth, accurate representation of what to do when soldering. May or may not have been soldering entirely incorrect lol

If you must insist on soldering.... use a small amount of paste flux on the wires to be joined together, that will help wick the solder into the joint in a matter of seconds. That will eliviate the extended time on the wire with the soldering iron so you are not melting the wire insulation ends trying to melt the solder getting it to flow. Be sure to use at least 70% isopropel alcohol to clean the flux off the joint afterwards, as its considered acidic, then use heat shrink tubing as always to seal the deal.

I just went out and did this on my car and it was really easy. Thanks for posting this man, it was really helpful :)

good video. reminds me of my journey through doing auto electrics in my car. Istarted off by doing crimps.. then moved up to soldering.. and then reverted back to crimps. very good to see the tool your using, it made me realise i need to upgrade mine to get it completely right.

You are an intelligent guy and you have excellent ability to explain how you arrive at a conclusion. Nonetheless, I will continue to solder when & where possible. However, after watching your presentation I have much greater trust in crimped connections.

Never had a problem with correctly soldered connections. Crimped connections work for a while but they develop surface corrosion between the wire and terminal over time. The corrosion interferes with conductivity and causes high resistance. Many electrical problems are the result.

If you´re working in the dashboard or other place inside the car´s habitacle crimping is acceptable although I always prefer soldering. But if you´re working outside the car´s habitacle when the wires are more exposed to the elements then soldering is definitely the way to go because copper and brass oxidize over the years increasing the joint´s resistance. If you´re worried about breaking the soldered joint just solder a smaller length with less solder wire and don´t stay all that time with the soldering iron in contact with the joint, this will result in spreading the solder into the wire´s interior ruining the flexibility. Make a smaller joint, use some solder paste flux to accelerate the soldering process and you will see that the flexibility of the soldered joint will be pretty much the same as a crimped joint. Add some heatshrink tube and you´re good to go. You don´t need nothing very fancy, just a normal soldering iron, paste flux and normal solder will do, no need for flux core solder if you´re using paste flux. The trick is to solder the joint only in a couple of seconds to avoid too much spreading of the solder. The wire will stay flexible and the connection will have low resistance pretty much forever.

What do you recommend for 8awg wire? I have a 12” DC level 5 sub (purchased it used) and the direct leads aren’t long enough to reach the (SMD) terminal cup. Thanks!

What do you do when you're trying to tap into existing OE wiring? crimps don't work unless you are willing to cut the original OE wire and then crimp two wires into one side of the crimp connector (the extra wire being the one you're adding to the circuit). Also, can't use heat shrink if you're not cutting the OE wire... I've seen people cut back the insulation on the OE wire and splice in the new wire with some fancy twists and then solder... do you avoid that as well?

"will never hold a soldering iron within 5 feet of a car".... is another way of saying.... "I can only park one vehicle in my two car garage". Quite a demonstration of character and commitment to ones convictions!

I like soldering. I do a good job of it and I cant recall anything I’ve ever soldered failing.

The only crimps that have ever worked consistently well for me are those bare copper ones they sell at Home Depot which look like little (maybe 1/4" to 3/8") segments of copper tubing. Everything else has seemed hit or miss, maybe because, as a DIYer I never develop a consistent habit of matching the crimps to the crimping tool. One other thing that has always worked perfectly for me was to cut the leads to different, complimentary lengths, so that the connections are offset from each other, then square-knot one pair, twist and tape it, square-knot the other pair, twist and tape that, then put either tape or heat shrink tubing around the whole thing. The knots guarantee a strong, permanent, self-tightening connection while the offset protects against shorts. The one caveat is that you have to know how to make a square knot with very short lengths of wire.

Hi, I'm converting a few of my early 1994 Harley-Davidson Molex connectors to Deutch. I discovered one of the ports has 2 wires going into it. I would imagine that trying to force 2 wires into one of the Deutch connectors is a "no-no"? In my case would it be best to peel back some of the insulation and soldier the two together and then use one port? Can't seem to find an answer to this. Thanks for sharing your thoughts and advice. I hope my above question made sense.

Great work with experiments to prove it!

I agree completely on the open barrel crimps and terminals. Far superior. And if you really want a reliable, low resistance connection, solder the ends of the wires together at the middle of the open barrel crimp connector. That is a connection that can’t be beat either electrically or mechanically.

Try Marine Grade inline splices and such. Not only do they have heat shrink built onto them they also have a sealer in them too. If you solder correctly you won't have long stretches of 'hard' wire. Soldering is best used for signal voltages to/from the computer. O2 sensor, etc where even a little resistance can cause problems.

I am thankful for this i need this because i am faced with having to fix a wire connection on my truck, and i havent even started to study and learn soldering, so i need something i can do without making this job my first soldering project. So i am using this for my truck this time...then after i have learned and experianced soldering then i can choosenthe best for my future projects on and of the vehical

I have three crimping tools, not one of them will crimp terminals tight enough so that pulling on them will not pull them apart. Soldering is a different matter, pull as much as you like, the terminal will not come apart. Look at any crimped joint that has been in use for a while, the joint is full of crud, you'll also notice frayed wires, not with soldered terminals. It is often said soldering is no good because the copper hardens and the copper wire will fracture because it is not flexible. That's true, however, the copper only hardens for around 10-12mm after the terminal. Who the hell leaves as little cable as that free. Typically, in cars there is 10 times that amount of free cable after a terminal. Crimp terminals are rubbish and for amateurs. If you want a strong, weatherproof and professional looking terminal, solder it and apply heatshrink. I use crimp terminal, but rather than crimp them, I remove the plastic insulating material, solder the wires in place and apply heatshrink. For non insulated terminals, I crimp them small joint, then solder it, then crimp the larger joint around the insulation. I've been doing it this way on cars and bikes for over 50years, I've. Never had one failure. Wish I could say the same for crimp connections applied by auto electricians. Crimp terminals are used commercially because it is simply the quickest and cheapest way of doing it. What do you want, a quick cheap connection that will eventually fail, or a proper, failsafe connection that will outlast you?

Great video, proper crimping goes a long way and is actually much faster than soldering. Another big one is using good connectors, DTM connectors can be purchased very cheaply (the crimpers for the pins are slightly more expensive) and work amazing leaving a very professional look

I’ve been an industrial robot technician for over 30 years. They move and vibrate on top of hard running machinery 24/7. We crimp connector pins because that is what they are designed for. For every other in line type wire connection we solder. I have never had or seen a properly soldered connection fail. NEVER. I have seen dozens of crimps fail.

Good info! I worked in electronics for 29 years and never used a nice crimp tool like yours. Had to use those thin one at a time crimp tool. would have saved a lot of time and trouble when repairing my printers and copiers.

Crimping or properly splicing a wire or connector gives you the mechanical hold, while soldering reinforces the electrical connection. As someone experienced in both automotive and electronic/electrical repair, I can guarantee that a spliced/crimped, soldered (PROPERLY!) and then protected (adhesive lined shrink wrap is my preference) is the most reliable, long term repair you can achieve. Where the problem lies is there are far too many hack soldering jobs where a booger of a cold solder joint is left hanging uninsulated as the sole "repair" to the connection, or the connection deteriorates and introduces way too much resistance into the circuit over time.

Ive seen more crimps come loose than i have proper solder joints in my 30 year tech career! Sorry your wrong!

The switch from lead-containing solder to no-lead solder has made soldering a lot more difficult, for me anyway. A lot of soldering tools, electric or butane, just don't seem to get hot enough for the new formulations, even though they're in the store right next to the no-lead solder. And no, I don't want to go back to the old style; I remember as a kid seeing that the age of death for electronic repairmen was relatively young compared to similar jobs for some unknown reason, and that bothered me, since I really liked repairing electronics.

whatever has the fewest amount of comebacks im down for. I have received those clearish/blue crimps before and have bins of them for a rainy day. Good upload and perspective

Your solder joint would not meet mil spec that is used in military application where function is paramount. Proper heatsinks near insulation will limit solder wicking past insulation. You won't find nearly as many crimps on aircraft, spacecraft, or nuclear weapons as soldered joints. Any crimps will use documented calibration and pre/post sample crimps for pull testing verification. There is a reason that I had to certify soldering when I was in the service. Never had crimping certification. Never had a proper solder joint fail on many automotive applications and did so many times to repair crimp joints that were intermittent and difficult to diagnose. The repeated bending/flexing of crimps are just as likely to fail as a solder joint. Ever heard of a strain relief? Crimps are more convenient than soldering, but don't say NEVER solder!

I've noticed that some of the cheaper non-heat shrink insulated butt connectors have a split seam (which is hard to see from the ends) that runs the length of the connector, and I think it's important to clock that seam to the top and bottom of the crimper jaws. If you have the seam on one side or the other, it ends up in a weaker flattened out "C"/clamshell shaped crimp that is very weak. Usually when I have a wire pull out of someone's previous work, it was crimped sideways with weak crimpers.

Very nice Video, I would like to add , the best electrical connection possible between two wires is a properly sized and properly executed crimp connector. any addition of solder only raises the resistance of the connection which is never a good thing, epoxy lined heat shrink tubing is necessary for any connection exposed to the elements. 40 years of repair of Electric motors, Transformers, And hobbyist in high end Vacuum tube Audio Systems.

Everyone can calm down, both crimping and soldering is effective if done correctly. ECM's in your car have solder, wiring harness connector pins have crimp. I have seen both fail equally from factory parts. When soldering I add Flux to the wires first, then cross strand wires together, heat wire and touch solder to other side not touching solder to iron tip. I make sure it soaks into the wires fully but don't gob it. After I use quality heatshrink but put dielectric grease around soldered wires before shrinking the shrink tubing over it. This prevents corrosion and further waterproofing. Crimping I use heat shrink. I've also used self soldering shrink butt connectors with no issues.

Ive had my shop for 15 years. (Auto repair/Inspections etc.) My 550hp Eclipse was wire tucked in 2010 with soldering, no issue to this day. It wouldnt be proper practice to assume crimping every single wire splice of an ECM is OK. One of the major components to a good solder is the amount of solder used. Too much, more cracking. Too much, more resistance. Too little, .... safer! In this video, you applied twice as much solder as I would. Excellent video, glad to see you practice for perfection!

16:50 Wow! The electrical current will be very happy knowing that the wire it cruises through can hold so much weight 😜😉. But jokes aside, mechanical strength is important, but so are the electrical characteristics. Although I am a fan of crimping when it comes to high power (especially high current) connections, I do prefer soldering for low power applications, such as digital and analogue signal cables. And let's face it: crimped connections are as susceptible to breaking on the edges as are the soldered ones. Without proper strain relief both are pretty much the same. It wasn't a bad video and I can agree with most of your claims, but: 1. you are waaaay to wary of soldering. Come on, mate! It's electronics 101! It is not that hard. On the contrary: once you know the proper basics, it's quite hard to botch. Even with a cheap, crappy soldering iron. Heck! Even with a lighter and a bottle cap! 2. If you want to make a really good comparison between soldered and crimped joints, do some electrical comparison as well. I admit: mechanical strength is important, but it's only a half of the story. Get a thermometer (thermocouple or thermovision camera), put some amps over the connection and measure the temperature. Do that a couple of times (at least 20-odd) each time giving the connection some time to properly cool off and then gather the results. Lousy crimped connection can be just as useless/dangerous as a bad soldering. Sometimes even more so, because it “looks nice” weather it was done correctly or not. “Tug test” may also be inconclusive although it's not useless either. Anyhow, if the connection wasn't crimped strongly enough to form a proper “cold-weld” it will degrade over time much quicker than any soldered joint.

What would you recommend for joining airbag wires. Mine broke in changing them and bought replacements

I've been soldering and crimping auto wires for 50 years and no problems, depends on the location. If the soldered joint is part of a bunched loom then vibration won't be a problem as the repaired wire is supported by all the other cables Even if the joint isn't waterproof (which it should be in cars) a correctly soldered joint will survive. The wire around it will rot leaving the solder joint still intact.⚠️ The ultimate joint would be a soldered crimp which I carry out if heavy currents are involved like on starter circuits or glow plug ccts. Very good demo at the end though. Fair play to ya 👏

All method will work. 1. Twist wires together. 2. Twist and solder. 3. Crimp. All method work just fine. Consideration on what method to use come up only when you are doing 100T joints. 😁😁😁 Then crimping is the hands down winner. Don't get distracted by lengthy discussion, we just want get home for dinner,

I am impressed by the quality of the crimp you produced and will explore it further. I am an old solder guy. I use a 12 volt soldering iron that crimps onto the battery.

I crimp wires all the time and I’ve never had a problem with the crimp or butt connectors unless I got cheap butt connectors. That happened once with a pack from Amazon but I noticed right away with the tug test when it wouldn’t hold the wire from pulling out. They were too thin and wouldn’t hold the squeeze. Other than that the only other issue is heat shrink connectors even with using a insulated section to crimp it they would cause a small Knick in the insulation and eventually corrode at the crimp point from salt. Just my personal experience. I’ve been getting some open barrel stuff lately to see if I like it more than closed terminals. I’ve never used them.

Bro, this is the best way to join two automotive wires! Been doing it for years and you just can't get better 👌 all these comments 'I've been soldering for 30 years...bla bla bla' are stubborn and aren't interested in change. Yes solder works but crimping is the ultimate, you won't find a solder joint on any OE manufactured vehicle today!

This video made me hit the subscribe button. As a professional auto electrician I can't stress how important it is to stay away from joining wires in a car with solder. The amount of time I spend fixing broken and corroded soldering jobs on cars makes me want to go around destroying soldering irons...

Thanks I needed this video. Even though I used the solder techniques you show for a great solder, a lot of the times on the vehicles it really isn’t great for me especially in hard to reach places and flexible places which is 90% of the car. I was just always under the impression that crimping was lazy, cheap and not weather proof. I’m definitely going to do that a lot more now, even got one of those expensive auto crimpers!

THANK YOU for encouraging younger generations to take the extra time and do the work RIGHT.

This is a great video, but you forgot to mention something. Never, ever, ever, marry a stripper.

It is difficult learn how to solder, but the solder joint done properly, is the better electrical joint.

But how would you accomplish tapping into an existing wire that you didn't want to cut, using the crimping method?

What brand wire crimpers were you using to do both crimps using open barrel crimps....also what is this stuff about low resistence vrs high resistance between solder and crimping and which is better for lower resistance

Lack of soldering almost caused a fire in my car. Always solder properly. If you can't, find someone who can (been soldering for over 50 years).

ASE Master technician here and I'll tell you what I was taught at the GM Training College in Atlanta. *Soldering is not necessary and introduces problems that crimping doesn't.* One thing anybody can see: Look at the wiring on any new car and you will not find any place where the manufacturer used solder.

Thanks! My Google search for "should I solder or crimp wires" ended here. Thanks a lot, Irvin.

I don't know if anyone else commented this, but on the Tip maintenance, one thing I run into a lot, Is that people don't know is that the tips of a iron actually have a different metal plating at the tip. While tinning is an important part, one SUPER IMPORTANT thing NOT to do is use sandpaper on your tip to clean it. If you remove that plating, your tip have several different issues (ie the solder will not stick to the tip and trouble heating, esp after the insulating oxidation layer forms). If you notice your tip, it has a nice clean line a bit back from the tip. This is a sign of a good tip with the plating still intact. But I've seen people who take sand paper to "clean" the tip ruining their tips and having trouble soldering because it's gone.

crimping over soldering? hahaha I can only imagine what the back of your cars head-unit looks like

Question? Can you use 3m corrosion protection coating after soldering the wires to ensure water stays out.

Wait... Are you using ignition sources in the same room as a gas heater?

NICE SMALL HEFTY LOOKING CRIMPER ! NOT THE FLIMSY NARROW ONES THAT I GOT FROM THE STORE. GREAT TUTORIAL! THANK YOU

You made your point very well. I would consider myself an expert solderer and I would caution trusting crimps on wires that are overheated and oxidized. In this case, rosin flux in solder still has an advantage over crimps. Perhaps there is an efficient way to prepare oxidized wires for crimping?

Great demonstration. I see you can get silver and gold colored cimps in the same pack. Why are there 2 types and how do you choose which one to use?

Another tip I never see talked about is Dielectric Grease. Ever hear of Galvanic corrosion, also called ' dissimilar metal corrosion? I used to have an older Honda and found the under hood connection were filled with a viscus thick clear grease. I later found out what it was, Dielectric Grease. Now I use it on almost every electrical connection. I like the Permatex brand in 3 oz size. One tube last forever. Here is an extreme example. I had some 500W halogen high power yard lights. The bulbs were only lasting a month or so. I filled each end of the bulb were it fits into the connector with Dielectric Grease. That bulb lasted almost 2 yrs. Due to heat and high voltage the bulb mount on each end was experiencing accelerated Galvanic corrosion to the point is would fail due to elevated resistance. It was Galvanic corrosion, also called ' dissimilar metal corrosion. The Dielectric Grease completely stopped this degradation due to oxidation and/or Galvanic corrosion. Almost every electrical connection will experience a slow increase in resistance specially if it is 2 different metals such as copper wire and a crimp on connector that is made from other metal, not copper. Almost every electrical connection has a limited life time unless it is actually soldered. The Dielectric Grease extends the crimp or bolt connection lifetime 100 fold as no oxidation and less Galvanic corrosion can occur. Just fill the connector and wires with a coat of Dielectric Grease then crimp it. Oh and don't forget to put dielectric grease on your battery terminals, every battery no matter what type benefits from this, Car battery and AAA batteries. I was having trouble with my small LED flashlights and dielectric grease helped. I think about the only battery I would not recommend dielectric grease on would be a watch battery. You would not want to take a chance on gumming up the moving parts with grease.

I use to solder EVERYTHING and swore by it. I have a great solder gun, shrink rap, cleaners, solder etc... I did some deep searching and found out why they don't use Solder in cars, and its exactly as you said, they are not flexible, and over time micro vibrations on cause things to crack and break (often times down inside the insulated part, not the joint). I've since been getting into building my own harness plugs, and also proper crimping. I've never had issues with solder on my own vehicles going strong for over 10 years now, but realize car manufactures use proper crimping over solder typically. I'm sure partt of this is for speed, however I also know that almost all cars electrical system (if untouched) will last well into the 100's of thousands of miles and decades of years without issues. I believe the more common issue, is not wrapping the cables, and letting them rub on a hard surface until the rubber has rubbed through. I now rate them as follows. 10/10: Proper Crimp 7/10: Solder 2/10: Improper Crimp Another tip, IF I use soldering on a car. I shrink wrap it again with a small zip tie in between the sealed solder and the wire, this will help keep the wire from ever being bent (and broken). Allowing it to bend on the standard strand wire where there is no solder instead. I usually follow it up with a decent amount of electrical tape. Works great if your doing a bunch of wires in the same spot, you can essentially make a "stiff" spot in the line where the soldered parts are, and not have to worry about things breaking as soon. If your doing this on a natural bend of the line... it is going to be risky, but if you have a straight portion it can help.